Abstract Permeability is a crucial parameter to describe the transport rate of a gas under pressure gradient, relevant to gas molecule movement in pores. The gas permeability of edible film, used on fresh or minimally processed fruits and vegetables, is an important parameter because it directly affects the product’s respiration rate and metabolic activity. The present study summarizes the principal methods for gas permeability measurement in edible films, considering methods developed at laboratory scale and the methods of the American Society for Testing and Materials Standards (ASTM), some of which have been adapted for edible films. The methods are classified as follows: gravimetric, differential pressure, and continuous flow. Gas permeability results depend heavily on the procedure achieved and laboratory conditions employed, as well as the preconditioning of the films before the tests.

RESUMEN Las fresas son frutas altamente perecederas, susceptibles a daño mecánico, deterioro y desórdenes fisiológicos durante su almacenamiento. La aplicación de recubrimientos, se presenta como una alternativa promisoria de tratamiento poscosecha, que permite mantener la calidad de las fresas. El objetivo de esta investigación fue estudiar el efecto de recubrimientos comestibles de sábila (A. vera) y alginato de sodio sobre parámetros de calidad de fresas, durante el almacenamiento refrigerado. Se evaluaron mezclas de recubrimientos comestibles de alginato de sodio y A. vera (100:0, 75:25, 50:50 y 25:75) sobre la pérdida de peso, color, firmeza, pH y acidez titulable de fresas, durante almacenamiento refrigerado (0, 3 ,9 y 12 días). Adicionalmente, se determinó el espesor y la opacidad de las películas obtenidas a partir de las soluciones formadoras de recubrimientos, utilizando el método de “casting”. Los resultados mostraron que la combinación de A. vera y alginato de sodio tiene un efecto significativo en la reducción de pérdida de calidad de fresa, durante el almacenamiento en refrigeración. Todos los tratamientos con recubrimientos comestibles presentaron, al final del almacenamiento, menor pérdida de peso (7-16%), mayor firmeza (entre 1,3 a 2,1 veces más), mayor retención del color y mayor acidez titulable que las muestras sin recubrimiento (control). El espesor de las películas disminuyó con el incremento de la adición de Aloe vera y la opacidad disminuyó significativamente con la adición de la sábila en 25% y 50% en las mezclas con alginato de sodio.

ABSTRACT Strawberries are highly perishable fruits, being susceptible to mechanical injury, decay and physiological disorders during storage. Applications of edible coatings have been shown to be promising as a tool to improve the quality and extend storage. The aim of this study was to evaluate the use of Aloe vera and sodium alginate as an edible coating in postharvest quality of cold storage strawberries. The composition of edible coatings of sodium alginate and A. vera (100: 0, 75:25, 50:50 and 25:75) was studied on weight loss, color, firmness, pH and titrable acidity of strawberries during refrigerated storage (0, 3, 9 and 12 days). The thickness and opacity of the films were also determined, from the coating forming solutions using the casting method. The short shelf life and the high deterioration of the quality characteristics of strawberries during postharvest, justify to investigate alternative conservation techniques such as edible coatings, in order to reduce food loss and improve consumer acceptance The results showed that the combination of Aloe vera and sodium alginate has a significant effect in the reduction of the loss of the quality of the fruit during refrigerated storage. All coating treatments showed at the end of storage less weigth loss (7-16%), greater firmness, (between 1,3 to 2,1 more times) more color retention and greater titrable acidity tan uncoated samples (Control). The addition of Aloe vera decreased the thickness of the films and the opacity decreased significantly with the addition of Aloe vera in 25 and 50% in the mixtures with sodium Alginate.

Resumen El objetivo de este trabajo fue evaluar la influencia de tratamientos osmóticos sobre la velocidad de congelación, pérdida de fase líquida (PFL), módulo elástico (ME) y esfuerzo del límite de fluencia (σL) en muestras de papaya (Carica papaya L.) almacenadas en congelación. La deshidratación se realizó con soluciones osmóticas de sacarosa de 45 y 55°Brix durante 30 y 90 min. Las muestras osmo-deshidratadas fueron congeladas a -40°C y almacenadas durante 10, 20, 30 y 60 días. Fruta fresca fue empleada como muestra control (No tratada). Los resultados mostraron que las muestras tratadas presentaron menores pérdidas de fase líquida respecto a las muestras control. El módulo elástico en las muestras tratadas presentó mayores valores en comparación con las muestras control. El esfuerzo del límite de fluencia disminuyó para todos los tratamientos durante el almacenamiento y las muestras tratadas mostraron valores superiores de σL respecto a las muestras no tratadas.

Abstract The aim of this study was to evaluate the influence of osmotic treatments on the freezing rate, drip loss (DL), elastic modulus (EM) and stress of yield limit (σL) of papaya (Carica papaya L.) samples stored under freezing conditions. Dehydration was performed using an osmotic sucrose solution with 55 and 45 ºBrix for 30 and 90 min. Osmotically dehydrated papaya samples were frozen at -40°C and stored for 10, 20, 30 and 60 days. Fresh fruit was used as a control sample during freezing storage. The results showed the treated samples exhibited lower drip loss with respect to control samples. It was observed that elastic modulus in treated samples showed higher values compared to control samples. Conversely, σL had achieved a decreasing for all treatments during freezing storage and treated samples exhibited higher σL values with respect to control samples.